  • 高瑞珍, 趙雨. 鉻鎳鉬銅高強度鑄鋼斷口缺陷分析[J]. 工程科學學報, 1984, 6(3): 23-33. DOI: 10.13374/j.issn1001-053x.1984.03.004
    引用本文: 高瑞珍, 趙雨. 鉻鎳鉬銅高強度鑄鋼斷口缺陷分析[J]. 工程科學學報, 1984, 6(3): 23-33. DOI: 10.13374/j.issn1001-053x.1984.03.004
    Gao Ruizhen, Zhao Yu. An Investigation of Fracture defect of Cast NiCrMoCu HSLA steel[J]. Chinese Journal of Engineering, 1984, 6(3): 23-33. DOI: 10.13374/j.issn1001-053x.1984.03.004
    Citation: Gao Ruizhen, Zhao Yu. An Investigation of Fracture defect of Cast NiCrMoCu HSLA steel[J]. Chinese Journal of Engineering, 1984, 6(3): 23-33. DOI: 10.13374/j.issn1001-053x.1984.03.004

    鉻鎳鉬銅高強度鑄鋼斷口缺陷分析

    An Investigation of Fracture defect of Cast NiCrMoCu HSLA steel

    • 摘要: 在鎳鉻鉬銅低合金高強度鑄鋼的生產中經常因出現異常斷口而降低鑄件的塑性和韌性。這種斷口缺陷無法用熱處理辦法消除。作為一種冶金缺陷,探討其產生的原因和消除辦法是生產急待解決的問題。本文以掃描電鏡為主要工具,對這種斷口的性質、特征和產生的原因作了初步探討。
      實驗的結果認為:鉻鎳鉬銅低合金高強度鑄鋼中的異常斷口為貝殼狀斷口。它的宏斷形貌是淡灰色無金屬光澤的碎石狀粗晶組織,微觀形貌是大小不等的韌窩,屬于韌性晶界斷裂。
      產生貝殼狀斷口的原因是第二類硫化物和氮化鈦的沿晶分布,它降低了晶間結合力并作為裂紋的核心,促使晶間斷裂的產生和發展。
      加入稀土和硅鈣可以控制硫化物形態和消除貝殼狀斷口。

       

      Abstract: The toughness and ductility of cast NiCrMoCu HSLA steel are dec-reased due to the existence of fracture defect during fabrication. The fracture appearance, non-metallic inclusions and the segregation of alloy elements have been investigated by means of microprobe analysis and scanning electron microscope.
      The results indicate that the fracture defect of cast HSLA steel is the conchoidal fracture. Its macrofracture appearance consists of bright gray, non-metallic lustrous and coarse grain structure. Its microstruc-ture appearance consists of dimples. This is ductile intergranular fracture.
      The conchiodal fracture is caused by the I type MnS and the TiN along the austenite grain boundaries. They become fracture origins, reduce intergranular cohesion force and promote the propagation of intergranular cracks.
      The modification of MnS inclusions and elimination of the conchoidal fracture are carried out by addition of RE and SiCa into the steel.

       

    /

    返回文章
    返回
  • <noscript id="y4y0w"><source id="y4y0w"></source></noscript>
    <table id="y4y0w"><option id="y4y0w"></option></table>
  • <li id="y4y0w"></li>
    <noscript id="y4y0w"></noscript>
    <noscript id="y4y0w"><kbd id="y4y0w"></kbd></noscript>
    <noscript id="y4y0w"><source id="y4y0w"></source></noscript>
    <menu id="y4y0w"></menu>
    <table id="y4y0w"><rt id="y4y0w"></rt></table>
  • 啪啪啪视频