Abstract: Recrystalization of the dispersion strengthened fetrihc steels, which was manufacted through chemical socking, was systemahcally studied. It was found that the recrystaization temperatures varied from 750 to 780 ℃, fine grains could be obtained by annealing after high-level deformation, grain boundaries of the grains with size smaller than limited value could be effectively Pinned by dispersoids, and Y₂Ti₂O₇ was stable during deformation and annealing.